Infiltration of Molten FeO-SiO<SUB>2</SUB> Slag into Pores in Al<SUB>2</SUB>O<SUB>3</SUB> Bricks with the Slagging Reaction
-
- WANIBE Yoshimoto
- Faculty of Engineering, Nagoya University
-
- YOKOYAMA Seiji
- Graduate School, Nagoya University, Now Toyohashi University of Technology
-
- ITOH Takashi
- Faculty of Engineering, Nagoya University
-
- FUJISAWA Toshiharu
- Faculty of Engineering, Nagoya University
-
- SAKAO Hiroshi
- Faculty of Engineering, Nagoya University
Bibliographic Information
- Other Title
-
- Al<SUB>2</SUB>O<SUB>3</SUB>-SiO<SUB>2</SUB>系れんがにおける気孔内への溶融FeO-SiO<SUB>2</SUB>スラグによる滓化反応を伴う浸透
- Al2O3-SiO2系れんがにおける気孔内への溶融FeO-SiO2スラグによる滓化反応を件う浸透
- Al2O3 SiO2ケイ レンガニオケル キコウナイ ヘ ノ ヨウユウ FeO
Search this article
Abstract
This study reveals the quantitative analysis on the infiltration of molten slag into pores in bricks with the slagging reactions. The experiment was carried out with an FeO-SiO2 slag on practically used Al2O3-SiO2 bricks at 1 523 and 1 573 K, then semi-theoretical formulations were introduced for the interpretation in a connected pores system. A satisfactory explanation was presented to the experimental observations on the slagging infiltration of the molten slag in the industrial bricks through the characterization of the pores system and the correlative evaluations of immersion force, slagging reactivity and wetting behavior. The unified interpretaion then suggests the possibility for the anticipative estimation of the phenomenon out of the material natures concerned.
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 73 (3), 491-497, 1987
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001205183208320
-
- NII Article ID
- 110001492019
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 3118927
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed