Effect of alloying elements of steel on the wettability between the steel melt and oxides was evaluated. Steels containing Ti, Nb, Mn and Al were melted on single-crystal and polycrystal plates of Al2O3 and MgO, and the contact angle between the melt and the oxide plate was measured. Titanium addition to steel was found to decrease the contact angle both on Al2O3 and MgO, but more titanium was needed to improve the wettability on MgO than on Al2O3. The addition of other elements, Nb, Mn and Al, did not improve the wettability between the steel melt and oxide plates. At the interface between Ti added well-wetted steel melt and oxide plate, reaction layer was formed. The layer was identified as Ti2O3 for 1% Ti added steel and TiO for 5% Ti added steel. Thermodynamic calculation supported the formation of these reaction products. It was concluded that the improvement of the wettability was achieved by the formation of the Ti-oxide reaction layers immediately after the melting of the steel and that the contact angles decreased depending mainly on the materials of reaction layers.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 92 (7), 411-416, 2006
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205183464576
-
- NII論文ID
- 110004731561
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 8009028
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可