冷間伸線加工をした準安定オーステナイト系ステンレス鋼における縦割れ

DOI Web Site Web Site 参考文献29件

書誌事項

タイトル別名
  • Longitudinal Cracking in Metastable Austenitic Stainless Steels during Cold Drawing
  • レイカンシンセン カコウ オ シタ ジュンアンテイ オーステナイトケイ ステンレス コウ ニ オケル タテ ワレ

この論文をさがす

抄録

Cracking parallel to the wire axis (longitudinal cracking) occurs during or after the drawing of metastable austenitic stainless steel wires. In this paper, the mechanism of cracking was investigated in relation to the behavior of deformation induced martensitic transformation, hydrogen content and residual stress in the steel wires drawn under different several conditions. Results obtained are as follows:<BR>(1) Martensite formed through deformation induced transformation is of lath-structure, but the lath-structure is broken and changed to dislocation cell structure during heavy drawing, which is characterized with the poor ductility.<BR>(2) Microcracks are formed around inclusions and carbide particles which are just in the heavily deformed martensite with dislocation cell structure. This leads to the cracking parallel to the wire axis.<BR>(3) Such a cracking occurs not only during drawing but also during aging at room temperature after drawing with the asist of residual stress and diffusive hydrogen.<BR>(4) Main reason for the cracking is thought to be stress concentration at inclusions and carbide particles which results in the formation of microcracks, and the structural change of martensite, existence of hydrogen and residual stress are secondary factors which promote the crack initiation.

収録刊行物

  • 鉄と鋼

    鉄と鋼 85 (3), 229-235, 1999

    一般社団法人 日本鉄鋼協会

参考文献 (29)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ