連続鋳造浸漬ノズルの介在物付着に及ぼす耐火物材質の影響と介在物付着モデルに基づく考察

書誌事項

タイトル別名
  • Effect of Refractory Materials on Inclusion Deposition of Immersion Nozzle in Continuous Casting and Mathematical Modeling of Inclusion Deposition
  • レンゾク チュウゾウ シンシ ノズル ノ カイザイブツ フチャク ニ オヨボス タイカブツ ザイシツ ノ エイキョウ ト カイザイブツ フチャク モデル ニ モトズク コウサツ

この論文をさがす

抄録

New immersion nozzle materials preventing inclusion deposition have been investigated by laboratory scale test. A new mathematical model has been proposed to explain the behavior of inclusion in the turbulent boundary layer near the nozzle and deposition rate of inclusions in the molten steel has been numerically evaluated.<BR>(1) The quantity of deposited inclusions has drastically decreased in the materials composed with high Al2O3 in comparison with Al2O3-C one. There is no deposition of inclusions on the material composed with pure Al2O3, (Sapphire).<BR>(2) About 30% of the inclusions less than 20μm in diameter reach at laminar sublayer and they are forced to move onto the refractory wall due to the interfacial tension gradient between inclusions and molten steel, formed by concentration gradient of silicon etc. in molten steel.<BR>(3) Deposition rate of inclusions in the molten steel was evaluated to be 0.75μm/s (1.35 mm thickness in 30 min) which is almost equal to the experimental results.

収録刊行物

  • 鉄と鋼

    鉄と鋼 85 (4), 307-313, 1999

    一般社団法人 日本鉄鋼協会

被引用文献 (11)*注記

もっと見る

参考文献 (32)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ