V,Nb添加9Cr-2Mo耐熱鋼の高温強度と靱性におよぼすC量の影響

DOI Web Site Web Site 被引用文献1件 参考文献1件

書誌事項

タイトル別名
  • Effect of Carbon on Creep Rupture Strength and Toughness of 9Cr-2Mo Heat-resisting Steels with V and Nb
  • V,Nb添加9Cr-2Mo耐熱鋼の高温強度と靭性におよぼすC量の影響
  • V Nb テンカ 9Cr 2Mo タイネツ コウ ノ コウオン キョウド ト

この論文をさがす

抄録

The effect of carbon on creep rupture properties and room-temperature toughness of (910)Cr-(1.82)Mo heat resisting steels with V and Nb was studied. The amount of carbon content was varied from 0.02% to 0.23% in order to improve toughness without decrease in creep rupture strength. The difference in creep rupture strength and Charpy absorbed energy between 10Cr-2Mo steels and 9Cr-1.8Mo steels was studied with respect to the ratio of δ-ferrite to martensite, the precipitates, and the microstructure.<BR>The results indicated that the 9Cr-1.8Mo-0.1V-0.05Nb steels with 0.05-0.14%C tempered at 800°C showed good toughness, and that 104h rupture strength of the steel was as high as that of SUS 316 at 550°Cand SUS 304 austenitic stainless steel at 600°C. It was concluded that the optimum amount of δ-ferrite with respect to both creep rupture strength and Charpy absorbed energy was 1020%.

収録刊行物

  • 鉄と鋼

    鉄と鋼 69 (16), 2037-2044, 1983

    一般社団法人 日本鉄鋼協会

被引用文献 (1)*注記

もっと見る

参考文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ