恒温圧延により微細化されたMg-Al合金,AZ91D板材の超塑性挙動

DOI Web Site Web Site 被引用文献3件 参考文献15件

書誌事項

タイトル別名
  • Superplastic Behavior in Mg-Al Alloy, AZ91D Grain Refined by Isothermal-rolling
  • コウオン アツエン ニ ヨリ ビサイカ サレタ Mg Al ゴウキン AZ91D イタザイ ノ チョウソセイ キョドウ

この論文をさがす

説明

Thin Mg-Al alloy, AZ91D sheets annealed around the temperature between 0% and 100% recrystallization have been prepared and tensed at high temperatures and with several strain-rates. Both the total elongation and strain-rate sensitivity m have been obtained and discussed.<BR>The values of total elongation have exceeded over 110% at all testing temperatures and with all strain-rates except high strain-rate at testing temperature of 573K, and the maximum total elongation of 270% has been obtained. The m values have indicated 0.5 in range of 1.0×10-4s1 to 2.5×10-4s-1 and maintained about 0.3 up to the neighborhood of 1.0 × 10-2s-1.<BR>The activation energy required for superplastic deformation has been calculated to be about 70 kJ·mol-1, which is almost same of the activation energy for self-diffusional grain boundary coefficient in Mg. Therefore, the superplastic deformation of AZ91D annealed around the temperature between 0% and 100% recrystallization has been accommodated by grain boundary diffusion.

収録刊行物

  • 鉄と鋼

    鉄と鋼 90 (1), 21-26, 2004

    一般社団法人 日本鉄鋼協会

被引用文献 (3)*注記

もっと見る

参考文献 (15)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ