- Behavior of Lubrication and Heat Transfer in Mold at High Speed Continuous Casting
- コウソク レンゾク チュウゾウジ ノ イガタナイ ジュンカツ デンネツ キョド
この論文をさがす
抄録
In order to cast high quality slabs with high productivity, high speed casting technology has been investigated with a pilot continuous casting machine capable of casting 50 to 100 tons of molten steel. The results can be summarized as follows;<BR>(1) High casting speed of 5.0 m/min for low carbon steel has been achieved with low viscosity powder. The powder consumption is small, from 0.1 to 0.2 kg/m2, but stable casting has been conducted.<BR>(2) Longitudinal crack has been occured even if for low carbon steel at up to 4.0 m/min. When the heat flux in mold increased critical value, longitudinal crack occured.<BR>(3) The control of the heat fluxes through the mold can be achieved by using the powder with appropriate properties.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 83 (11), 701-706, 1997
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205184330240
-
- NII論文ID
- 110001481612
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 4334631
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可