爆着チタン・ステンレスクラッド鋼板の熱処理による接合特性の変化とTiC炭化物の拡散バリア効果

DOI 機関リポジトリ 機関リポジトリ (HANDLE) Web Site Web Site 被引用文献4件 参考文献23件 オープンアクセス

書誌事項

タイトル別名
  • Diffusion Barrier Effect of TiC Layer Formed at the Bonding Interface and Bonding Characteristics of an Explosively Welded Ti/SUS420J1 Stainless Steel Clad by Heat Treatment
  • バクチャク チタン ステンレス クラッド コウハン ノ ネツ ショリ ニヨル

この論文をさがす

説明

The high temperature stability of an explosively welded Ti/SUS420J1 stainless steel clad was assessed by studying microstructures and bonding strengths of the clads with changing the annealing temperature. Compounds formed at their bonding interfaces consisted of TiC, FeTi, and/or Fe2Ti phases depending on the annealing conditions. The TiC layer formed at the boundary acts as an barrier for the diffusion of the base metals across the bonding interface under the 1000°C annealing and prevents the growth of intermetallic compounds, (FeTi and Fe2Ti) and of β-Ti. The specimens formed TiC layer at the bonding interface sustained high bonding strength even by high temperature annealing. Diffusion barrier effect diminished above 1050°C annealing due to the dissolution of TiC layer in γ matrix and the strength decreased. The diffusion barrier effect of the TiC layer was discussed on the basis of phase diagrams and physical properties of TiC compound.

収録刊行物

  • 鉄と鋼

    鉄と鋼 83 (11), 736-741, 1997

    一般社団法人 日本鉄鋼協会

被引用文献 (4)*注記

もっと見る

参考文献 (23)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ