焼結鉱の軟化溶融性状評価法の開発

DOI Web Site Web Site 被引用文献13件 参考文献8件

書誌事項

タイトル別名
  • Development of Evaluation Method for Softening-melting Properties of Sinter
  • ショウケツコウ ノ ナンカ ヨウユウ セイジョウ ヒョウカホウ ノ カイハツ

この論文をさがす

抄録

In order to clarify the sinter properties desirable for blast furnace operation, a new measuring apparatus with a gas preheater has been developed. This apparatus can raise a gas temperature up to 1700°C and conduct an adiabatic heating control. Using this apparatus, it is possible to detect the heating and reduction delay of sinter due to a rapid endothermic reduction of molten FeO.<BR>As a result of the experiments by using sinter samples produced by a sintering pot, the sinter having a low bulk density and a large amount of micro pores shows a high reduction degree at 1200°C.<BR>A new evaluation method has been presented to determine the sinter properties related to the permeability of cohesive layer in the blast furnace. In this method, five indices which need to have values with certain ranges are selected.<BR>The sinter desirable for blast furnace operation should have a low SiO2 content when CaO/SiO2 is high. This means that a sinter should have a low slag volume with a high melting point in order to form a permeable cohesive layer.<BR>Further studies are necessary to measure the actual sinter properties and verify the validity of this method by analyzing the relation between these indices and the results of the blast furnace operation.

収録刊行物

  • 鉄と鋼

    鉄と鋼 83 (2), 97-102, 1997

    一般社団法人 日本鉄鋼協会

被引用文献 (13)*注記

もっと見る

参考文献 (8)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ