Transport Phenomenon of Oxygen through Molten CaO-SiO<SUB>2</SUB> System Containing Zinc and Nickel Oxides

DOI Web Site Web Site 1 Citations 2 References

Bibliographic Information

Other Title
  • 酸化亜鉛および酸化ニッケルを含有する溶融 CaO-SiO<SUB>2</SUB> 系酸化物中の酸素の輸送現象
  • 酸化亜鉛および酸化ニッケルを含有する溶融CaO-SiO2系酸化物中の酸素の輸送現象
  • サンカ アエン オヨビ サンカ ニッケル オ ガンユウスル ヨウユウ CaO

Search this article

Abstract

Oxygen transfer rates, P, through molten NiO-CaO-SiO2, ZnO-CaO-SiO2 and NiO-ZnO-CaO-SiO2 systems were measured by using a molten thin film penetration method developed by the author. Temperatures of the measurement were about 1 450, 1 500 and 1 550°C.<BR>The transfer rates were 1 to 5 time 10-8 mol·O2·cm-1·s-1. They were the same order of the magnitude as that in the case of iron oxide-CaO-SiO2 system measured previously. In the case of system containing NiO, the more NiO contents the higher oxygen transfer rate. On the other hand, in the case of system containing ZnO, the higher ZnO contents the higher oxygen transfer rate in the case of less than 20mol%ZnO and the higher ZnO contents the lower oxygen transfer rate in the case of more than 20%ZnO.<BR>Effects of constituent on oxygen transfer rate, P, with the unit of mol O2·cm-1·s-1 are empirically expressed as follows:<BR>System less than 12.5 mol% NiO : P = 3.15×10-9 (mol%NiO)<BR>System less than 35mol% ZnO : P = -8.5×10-11 (mol%ZnO-22)2+4.2×10-8<BR>Temperature dependencies of the oxygen transfer rates are as follows:<BR>7.5 mol%NiO-46.3 mol%CaO-46.3 mol%SiO2 : P = 3.51×10-2 exp (-25.3×103 / T)<BR>10 mol%ZnO-45 mol%CaO-45 mol%SiO2 : P = 3.24×10-2 exp (-25.3×103 / T)<BR>20 mol%ZnO-40 mol%CaO-40 mol%SiO2 : P = 6.39×10-2 exp (-25.3×103/ T)<BR>30 mol%ZnO-35 mol%CaO-35 mol%SiO2 : P = 4.96×10-2 exp (-25.3×103 / T)<BR>It was estimated that NiO and ZnO acted as p- and n-type semiconductors, respectively, on the basis of the discussion on the dependency of the transfer rate on oxygen partial pressure at the surface of the molten oxide.

Journal

  • Tetsu-to-Hagane

    Tetsu-to-Hagane 76 (2), 191-198, 1990

    The Iron and Steel Institute of Japan

Citations (1)*help

See more

References(2)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top