Leaching of Platinum from Cobalt-Rich Crust by Hydrochloric Acid with Hydrogen Peroxide
-
- WANG Li Pang
- The University of Tokyo, Department of Systems Innovation, Graduate School of Engineering
-
- SATO Daisuke
- The University of Tokyo, Department of Systems Innovation, Graduate School of Engineering
-
- DODBIBA Gjergj
- The University of Tokyo, Department of Systems Innovation, Graduate School of Engineering
-
- SADAKI Jun
- The University of Tokyo, Department of Systems Innovation, Graduate School of Engineering
-
- FUJITA Toyohisa
- The University of Tokyo, Department of Systems Innovation, Graduate School of Engineering
-
- HISHITA Hajime
- Japan Oil, Gas and Metals National Corporation
Bibliographic Information
- Other Title
-
- 塩酸および過酸化水素の添加によるコバルト・リッチ・クラストからの白金の浸出
- エンサン オヨビ カサンカ スイソ ノ テンカ ニ ヨル コバルト リッチ クラスト カラ ノ ハッキン ノ シンシュツ
Search this article
Description
Leaching of platinum (Pt) traces from Cobalt-Rich Crust (CRC) in hydrochloric acid (HCl) solution with hydrogen peroxide (H2O2) was carried out in this work. Two kinds of CRC samples with different Pt grades were used and the effects of HCl and H2O2 concentration, leaching temperature and time as well as solid-liquid ratio were investigated to evaluate the Pt leaching.<br> The results showed that more than 95% of Pt in the CRC sample was leached out in HCl solution which concentration was more than 2 mol/L. The leaching temperature was higher than 50°C and the time was longer than 30 min whereas the solid-liquid ratio was less than 50 g/L. Similar results were observed when using HCl solution of more than 0.5 mol/L with the addition of more than 1 vol.% H2O2, while the leaching temperature was kept at 30°C and the time was longer than 15 min but at a reduced solid-liquid ratio (i.e. less than 10 g/L). There was no difference on Pt leached fraction between the two CRC samples with different Pt grades.<br>
Journal
-
- Resources Processing
-
Resources Processing 56 (4), 165-173, 2009
The Resources Processing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205206504576
-
- NII Article ID
- 130000137821
-
- NII Book ID
- AA11907992
-
- ISSN
- 13499262
- 13486012
-
- NDL BIB ID
- 10496548
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed