<p>Voids formation by cementite was investigated quantitatively in high strength steel sheets consisting of bainitic ferrite and cementite. Tensile tests were performed with rectangular specimen in longitudinal direction to rolling direction. After the tensile tests, the fractured specimens were cut along the width center. The cross sections near the fractured surface were observed by SEM. Voids and microstructure were observed in five thickness reduction areas with different strain level. As a result, number density of voids increased as strain increased. Not only the number of short voids observed in low strain but also the number of long voids increased as strain increased. Mainly, two types of voids were seen here. One was decohesion of interface between bainitic ferrite and cementite, and the other was cracking of cementite itself. Misorientation in the crystal grains was determined by KAM (Kernel Average Misorientation) using EBSD analysis. The obtained KAM values increased as strain increased, especially in the boundaries between bainitic ferrite and cementite. Therefore, it was revealed quantitatively that voids formed mainly through local strain increase.</p>
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 103 (8), 483-490, 2017
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205214960640
-
- NII論文ID
- 130005874170
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 028446834
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可