- A Study on the New Blowing Method in the Decarburization Process of Pretreated Hot Metal
- ヨビ ショリ ヨウセン ノ ダッタン プロセス ニ オケル シン スイレンホウ
この論文をさがす
抄録
Decarburization of pretreated hot metal with less slag was studied by use of a 10 t ladle type travelling furnace based on a new idea. The characteristics of refining and the mechanism of post combustion of off gas were discussed.<BR>(1) In spite of deep bath (L0/D= 1.0) in the furnace, molten steel was not overoxidized in the case that the flow rate of argon blown from the bottom was more than 0.05 Nm3/min·t with super soft oxygen top blowing (L≅100 mm).<BR>(2) In this method, the post combustion ratio (CO2/(CO+CO2)) was very high, so the high temperature rising, almost 200°C/%C, was obtained.This decarburization furnace had large flexibility for heat balance.<BR>(3) On post combustion, the parameter K (=(ΣiSi+αΣjSj')×3600/(FO2+ FO2')) was proposed and the mechanism could be explained by this parameter K on this ladle type furnace and the conventional top and bottom blowing converter.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 73 (6), 645-652, 1987
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205215673728
-
- NII論文ID
- 110001492044
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3120267
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可