欠陥スピネル粉末からの酸化亜鉛の真空蒸発

DOI Web Site Web Site

書誌事項

タイトル別名
  • Vaporization of zinc oxide from defective spinel powders in vacuum.
  • 欠陥スピネル粉末からの酸化亜鉛の真空蒸発〔英文〕
  • ケッカン スピネル フンマツ カラ ノ サンカ アエン ノ シンクウ ジョウハツ 〔 エイブン 〕

この論文をさがす

抄録

The mechanism for the vaporization of ZnO from powders of (Zn0.2Co0.8)O⋅1.1Al2O3 and (Zn0.2Ni0.8)O⋅1.1Al2O3 spinels was studied at 1335° to 1500°C in vacuum of 3×10-5 to 10-4 Torr. The vaporization of ZnO occurred in two stages-vaporization of constant rate at the first stage and of decreasing rate at the second stage. The observed fractions of ZnO vaporized deviated from the calculated values at higher temperatures. The results were interpreted with the assumption that the exsoluted corundum layer at the powder surface sintered more densely at higher temperatures causing the decrease in vaporization surface area. The ratio of the concentration of ZnO at the surface to the initial concentration at the time the vaporization mechanism changed from the first to the second stage was approximately 0.9 and independent of temperature.

収録刊行物

  • 窯業協會誌

    窯業協會誌 87 (1003), 153-157, 1979

    公益社団法人 日本セラミックス協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ