The failure probability of the ceramics in use which are proved their life time by a proof test was studied on the basis of the fracture mechanics of ceramics. Especially the influence of the safety factor, k, for the level of test stress on the probability was studied. The study proved that the probability depends much on the value of n, m, g and k, where n is the material constant connecting the crack propagation velocity v and the stress intensity factor KI as v=AKIn, m is Weibull modules, g is the ratio of the required fracture stress of the ceramics to possess the required life time, σg, to the mean fracture stress, σ, (σg=g·σ), and k is the safety factor or the ratio of the test stress, σk, to σg (σk=k·σg). And it was shown that the probability is the minimum at the optimum value of k, and that the probability can be 1ppm or less at suitable values of k (1.2-1.5), in most ceramics having n-80, m-15 and g-0.5 or less. The efficiency of the proof test, however, is not always so high, especially for the ceramics of low n. Therefore, some care must be paid on the application of the test.

収録刊行物

  • 窯業協會誌

    窯業協會誌 92 (1065), 281-287, 1984

    公益社団法人 日本セラミックス協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ