- Effect of Precipitation Behavior of AlN on Abnormal Growth of Ferrite Grains in Low-carbon Steel Wires
- テイ タンソ コウセン ノ ヤキナマシ ニ オケル イジョウリュウ セイチョウ
この論文をさがす
抄録
Abnormal growth of ferrite grains in low-carbon steel wires (C<0.04%) was studied from the viewpoint of AlN precipitation during annealing after cold drawing of 70.2% in reduction.<BR>(1) Abnormal grain growth occurred when Al/N ratio of steel wires decreased to the range from 1 to 6.<BR>(2) AlN precipitation in wire rod within above range of Al/N ratio was delayed in the course of cooling after the hot rolling, followed with fine AlN precipitations during recrystallization and grain growth at annealing stage after drawing. Such precipitates generated a large restraining force on the grain boundary movement and grain growth was completely depressed. In the case of the isothermal annealing at 800°C, however, abnormal grain growth occurred in accordance with decrease in the restraining force as a result of the coalescence of AlN precipitates immediately after the precipitation had been completed.<BR>(3) The critical conditions investigated for the abnormal grain growth initiating in the restrained grains were in good agreement with HILLERT'S theoretical expectations.<BR>(4) The restraining force of the fine precipitates on the grain boundary movement can be evaluated as follows :<BR>s=f;(1-log f;2)σ/3r<BR>where s is the restraining force ; r and ƒ are radius and volume fraction of the second phase particles, respectively ; σ is the grain boundary energy.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 70 (15), 2001-2008, 1984
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205216937216
-
- NII論文ID
- 110001490583
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 3008816
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可