弁ばねの疲労破壊の進展

DOI Web Site Web Site

書誌事項

タイトル別名
  • The Fatigue Fracture Progress of Valve Springs
  • ベンバネ ノ ヒロウ ハカイ ノ シンテン

この論文をさがす

説明

By using new technique which enables us to measure the depth of initial fatigue cracks in springs, the mechanism of fatigue on engine valve springs was made clear:<br>(1) The initial cracks on non-electropolished springs start from the surface of wire. By contraries, on electropolished springs, they start from inside of wire.<br>(2) On non-electropolished spring, the depth of initial cracks has certain critical values, which probably depend on applied stress.<br>(3) When the initial crack on non-electropolished springs reaches the critical depth, failure occurs suddenly. On the other hands, when the initial crack on electropolished springs comes to surface, sudden failure takes place.

収録刊行物

  • ばね論文集

    ばね論文集 1996 (41), 7-11, 1996-03-31

    日本ばね学会

キーワード