合成フォルステライト焼結体の高温物性

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Sintering and high temperature properties of synthesized forsterite.
  • ゴウセイ フォルステライト ショウケツタイ ノ コウオン ブッセイ

この論文をさがす

説明

In the synthesis of forsterite from magnesia and silica, the sintering conditions giving onephase forsterite have been determined as follows;<br>a mixture of stoichiometric magnesia and silica, to which titania and methylcellulose are added as a sintering accelerator and binder respectively, is molded at 500kg/cm2 and then fired for 1h at 1600°C. The sintered body of synthetic forsterite so prepared had the following physical properties:<br>(1) the average hot modulus of rupture: 396kg/cm2, (2) the thermal conductivity is inversely preportional to temperature and is 2.14kcal/m·h·°C at 700°C, (3) the thermal expansion coefficient: 13×10-6deg-1 and (4) the modulus of elasticity: 4.6×105kg/cm2.

収録刊行物

  • 窯業協會誌

    窯業協會誌 92 (1072), 719-725, 1984