Na<SUB><I>x</I></SUB>CoO<SUB>2 - δ</SUB> 単結晶を用いたテンプレート粒成長法及び反応性テンプレート粒成長法により合成した高配向 Na<SUB><I>x</I></SUB>CoO<SUB>2 - δ</SUB> セラミックス
書誌事項
- タイトル別名
-
- Highly Textured NaxCoO2-.DELTA. Ceramics Fabricated by Both Templated Grain Growth and Reactive Templated Grain Growth Methods Using Single-Crystalline Particles as Templates
- Highly Textured NaxCoO2-δ Ceramics Fabricated by Both Templated Grain Growth and Reactive Templated Grain Growth Methods Using Single-Crystalline Particles as Templates
- Highly Textured NaxCoO2 デルタ Ceramics Fabricated by Both Templated Grain Growth and Reactive Templated Grain Growth Methods Using Single Crystalline Particles as Templates
この論文をさがす
抄録
Textured γ-NaxCoO2 - δ ceramics have been prepared by both templated grain growth (TGG) and reactive templated grain growth (RTGG) methods using single-crystalline particles of γ-NaxCoO2 - δ as templates. An XRD analysis indicated that the samples were highly c-axis oriented; i.e., the highest Lotgering’s factor was estimated to be 0.93. According to transport property measurements, the highly textured γ-NaxCoO2 - δ sample exhibited electrical conductivity (σ) = ∼1.85 × 104 S/m, Seebeck coefficient (S) = ∼137 μV/K and power factor (PF ≡ σ·S2) = 0.35 mW·m-1·K-2 at ∼800 K. These values of σ and S are smaller than those of single crystals (sc) ; that is, σsc = 19.2 × 104 S/m and Ssc = 200 μV/K at 800 K. The magnitude of σ was found to decrease in proportion to the relative density (d) of the sample, while S was independent of d. Furthermore, both σ and S seemed to be sensitive to the Na content of the samples. Both the low density(d∼70%) and the deviation from the optimal Na content were considered to be predominant factors for the low thermoelectric properties of the present textured samples.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 111 (1292), 227-231, 2003
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205247785984
-
- NII論文ID
- 110002288045
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 6530792
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可