書誌事項
- タイトル別名
-
- Thick-Film Capacitors Made from Glass-Ceramics Containing PbO and TiO<sub>2</sub>
- PbO , TiO2 オ ガンユウ スル ガラス セラミックス ユウデンタイ ニ ヨル コウマク ヨウリョウ ソシ エイブン
この論文をさがす
説明
1) A thick-film capacitor having a dielectric constant of 94 and tan δ of 0.0130 (at 106c/s) was obtained by firing powder of a PbO-TiO2-Al2O3-SiO2-B2O3 glass on an alumina substrate to approximately 600°C. The layer of glass powder was changed to a glass-ceramic film in this firing process. The temperature dependence of the dielectric constant of the capacitor was almost linear in the range from room temperature to 270°C with temperature coefficient of 0.00083/degree.<br>2) It was found that glass powders which soften before crystallization are suitable for preparing capacitors of high dielectric constant. Otherwise, many cracks were formed in the thick-film dielectrics, which resulted in the lowering of its apparent dielectric constant.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 78 (894), 58-63, 1970
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205247816576
-
- NII論文ID
- 110002317035
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 8468307
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可