ニッケルフェライトにおける格子不整と飽和磁化

DOI Web Site Web Site

書誌事項

タイトル別名
  • Saturation Magnetization of Nickel Ferrites in Relation to Lattice Strain
  • ニッケル フェライト ニ オケル コウシ フセイ ト ホウワ ジカ

この論文をさがす

説明

Oxalate of Ni2+ and Fe2+ was co-precipitated by titrating an aqueous solution containing Ni2+ and Fe2+ (Ni/Fe=0.5) to an oxalic acid solution. The oxalate changed to nickel ferrite on firing at various temperatures from 500° to 1000°C in air. The nickel ferrite thus obtained was an Fe-deficient spinal-type phase, of which chemical composition can be written as Ni1.09Fe1.91O3.95 from the results of chemical analysis and density measurements. The analysis of X-ray diffraction line-broadening showed that the sample fired at fairly low temperatures have many crystal imperfections such as lattice strain (Δd/d) and lattice defects, which decreased with increasing firing temperature and vanished above 800°C. The nickel ferrite having such crystal imperfections has a low saturation magnetization, which increased with increasing firing temperature. In order to clarify the relation between saturation magnetization and lattice imperfections, another sample of nickel ferrite, which was prepared by solid state reaction of NiO and Fe2O3, was mechanically ground for an extended tune period to introduce lattice strain. The saturation magnetization of the nickel ferrite thus obtained also decreased linearly with increasing lattice strain, as in the sample prepared by co-precipitation method. These facts suggest that the lattice strain, regardless of its origin, lowers the saturation magnetization.

収録刊行物

  • 窯業協會誌

    窯業協會誌 94 (1088), 393-399, 1986

    公益社団法人 日本セラミックス協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ