Li<sub>2</sub>O-SiO<sub>2</sub> 系透明結晶化ガラスの強度

DOI Web Site Web Site 被引用文献2件 参考文献15件
  • 森本 繁樹
    School of Ceramic Engineering, Institute of Engineering, Suranaree University of Technology,
  • WARAPORN EMEM
    School of Ceramic Engineering, Institute of Engineering, Suranaree University of Technology

書誌事項

タイトル別名
  • Strength of Li2O-SiO2-System Transparent Glass-Ceramics

この論文をさがす

説明

The relationship between fracture strength and crystal size in the Li2O-SiO2-system transparent glass-ceramics was investigated. The precipitated crystal phase, percent crystallinity and crystal size were Li2O•2SiO2, 60-80% and 20-60 nm, respectively, following heat treatment below 800°C for 5-144 h. It is found that fracture strength increases linearly with increasing crystal size in the range of 20-60 nm for both non abraded and abraded specimens. Fracture strength can be expressed as a function of crystal size, d (nm), by<br>σ=100.5+2.32d (MPa) [Non-abraded]<br>σ=56.3+0.99d (MPa) [Abraded]<br>This result shows the opposite tendency for previous result of glass-ceramics of micrometer order crystals. This indicates that very fine crystals cannot effectively interrupt crack propagation, and hence, the stress required for changing the direction of propagation might be small. It can be considered that a critical crystal size may exist for the attainment of the maximum strength.<br>

収録刊行物

被引用文献 (2)*注記

もっと見る

参考文献 (15)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ