Synthesis of AlN by the Nitridation of the Floating Al Particles in N<sub>2</sub> Gas
-
- HOTTA Noriyasu
- Department of Chemical Engineering, Faculty of Engineering, Niigata University
-
- KIMURA Isao
- Department of Chemical Engineering, Faculty of Engineering, Niigata University
-
- TSUKUNO Akihito
- Department of Chemical Engineering, Faculty of Engineering, Niigata University
-
- SAITO Natsukaze
- Department of Chemical Engineering, Faculty of Engineering, Niigata University
-
- MATSUO Shigetomo
- Department of Chemical Engineering, Faculty of Engineering, Niigata University Maeta Concrete Works, Ltd.
Bibliographic Information
- Other Title
-
- 浮上Al粒子の窒化反応によるAlNの合成
- フジョウ Al リュウシ ノ チッカ ハンノウ ニ ヨル AlN ノ ゴウセイ
Search this article
Description
The nitriding reaction of floating Al particles in N2 gas was studied at 1350°-1550°C. The hollow spherical and fibrous AlN's formed were examined by X-ray diffraction and scanning electron microscopy. The nitriding reaction of floating Al particles in N2 gas proceeded in the following four steps: (i) floating Al particles melted and became spherical by surface tension, (ii) up to 1350°C the nitriding reaction was controlled by the diffusion of nitrogen through the AlN surface layer, (iii) cracks propagated in the AlN layer at 1400°-1550°C. The nitriding reaction rapidly proceeded with the eruption of internally melted Al, (iv) the eruption of Al also caused the nitriding reaction between vaporized Al and N2 gas to form AlN, resulting in hollow spherical AlN and fibrous AlN. The synthesized AlN was white, indicative of high purity. Since the particle size of floating Al was determined by controlling the N2 gas velocity, the classification of Al particles was possible. The mean size and size distribution of hollow spherical AlN particles formed were controlled within the range 4 to 12μm. The hollow spherical AlN particles were so brittle that they were easily crushed to fine particles even by fingers. Thus obtained AlN particles were very fine and had narrow size distribution of 0.1-0.2μm.
Journal
-
- Journal of the Ceramic Association, Japan
-
Journal of the Ceramic Association, Japan 95 (1098), 274-277, 1987
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205248662784
-
- NII Article ID
- 110002313591
- 120006740471
-
- NII Book ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- HANDLE
- 10191/7460
-
- NDL BIB ID
- 3119032
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed