- Carbothermical Preparation of Aluminum-Iron Alloys
- タンソ ネツ カンゲンホウ ニ ヨル アルミニウム テツ ケイ ゴウキン ノ
この論文をさがす
抄録
A high yield of aluminum alloys was difficult to achieve with a blast furnace, because both heating samples and reducing samples were done in the same chamber. In this report, we achieved a high yield of Al-Fe alloys, 70wt%, by carbothermic reduction of Al2O3-Fe2O3-C samples using a new indirect heating method. The method for preparing the sample to be reduced was based on the reduction mechanism of alumina. The sample was prepared by mixing graphite powders (0.3-0.5mm) coated with fine α-Fe2O3 powders (1μm) and α-Al2O3 powders (20-80μm) and subsequent compaction.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1100), 453-455, 1987
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205248706176
-
- NII論文ID
- 110002313622
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3133082
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可