- Effect of Carbon Monoxide on the Sintering of SiC Whisker-Zirconia Composite
- SiC ウイスカー ジルコニア フクゴウケイ ノ ショウケツ ニ オケル CO
この論文をさがす
抄録
Reaction between silicon carbide and yttria-stabilized zirconia (YSZ) powders, ZrO2+3/2SiC=ZrC+3/2SiO(g)+1/2CO(g), was appreciable above 1400°C in argon atmospheres. The reaction was suppressed by adding an appropriate amount of carbon monoxide to the atmosphere. This finding was applied to the pressureless sintering of SiC whisker-YSZ composites. In CO (33%)-Ar atmosphere, 5vol% SiC whisker-YSZ composite densified to 97% theoretical density by pressureless sintering at 1550°C for 1h. At higher whisker contents, however, the sintered density of composite decreased with increasing whisker content in the same firing atmosphere, due to the formation of network structure by SiC whisker.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1106), 1040-1042, 1987
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205248958976
-
- NII論文ID
- 110002313734
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3156372
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可