ZrB2 was hot-pressed at the temperature range from 1450° to 1970°C with or without additions of 6% of metallic binders- Cr or Ni. Densification rates at constant pressure of 200kg/cm2 were measured continuously for about 30 min at each test temperature.<br>For the hot-pressing below the melting temperature of metallicbin der, these data were treated reasonably with following equation which were proposed by Murray et al. for the plastic flow model of hot-pressing ceramics.<br>dD/dt=(3P/4η)(1-D) and integrating, <br>ln(1-D)=-(3P/4η)t+ln (1-D0).<br>Viscosity, η, was calculated at various temperatures for ZrB2 compacts. Activation energy was about 85kcal/mol.<br>In case when ZrB2-metal mixtures were hot-pressed above melting temperatures of metals, porous surface layers were observed with deficiency in metallic binder and with deviation of densification data from Murray's epuation.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 75 (859), 84-90, 1967
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205249787264
-
- NII論文ID
- 110002304218
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 8468124
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可