α・Al<sub>2</sub>O<sub>3</sub>を含むムライト焼結塊からなる粒とNa<sub>2</sub>O・2SiO<sub>2</sub>ガラスとの加熱反応
書誌事項
- タイトル別名
-
- Reaction Between the Sintered Mullite Particle Containing α-Al<sub>2</sub>O<sub>3</sub> and Na<sub>2</sub>O⋅2SiO<sub>2</sub> Glass
- アルファ-Al2O3 オ フクム ムライト ショウケツカイ カラ ナル ツブ ト Na2O 2SiO2 ガラス ト ノ カネツ ハンノウ
この論文をさがす
説明
In order to examine the change of composition in the matrix of fire clay refractory during heating, the reaction between α-Al2O3 containing mullite particle and Na2O⋅2SiO2 glass was studied with varied temperatures from I hr to 96 hrs.<br>Obtained results were as follows;<br>1) The dissolution process of mullite into glass is the first order reaction in the heating procedure of 36-64 hrs and its activation energy was ca. 50kcal/mol. In the case of longer heating time, diffusion rate of mullite particle into glass was saturated.<br>2) The content of α-Al2O3 in the particle increased slightly with the heating time.<br>3) In the process of reaction between mullite particle and Na2O⋅2SiO2 glass, both nephelite and carnegieite deposited. The amout of nephelite decreased with the rise of temperature, but that of carnegieite was affected by the amount of Na2O⋅2SiO2 glass and heating temperature.<br>Especially, the less the amount of glass added, the more the amount of carnegieite increased with the heating temperature.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 75 (859), 70-73, 1967
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205249811456
-
- NII論文ID
- 110002304215
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 8468121
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可