- Effect of Glass Composition on Formation of Double Layer Consisted of Conventional Glaze and Glass for Sanitary Ware
- エイセイ トウキ ジョウ ノ ユウヤク ガラス 2ソウ コウゾウ ニ オヨボス ガラス ソセイ ノ エイキョウ
この論文をさがす
抄録
The surface of a conventional sanitary ware was covered with the glaze that was a glassy phase containing silica and zircon crystals. Therefore, the surface of the glassy region was eroded selectively by using it for long time, which made a rough surface of a sanitary ware that causes adhesion of dirt on the surface. In this study, we investigated a double layer structure constituted of a conventional graze layer and a coating glass layer on the sanitary ware surface for improvement of durability and anti-contamination of the sanitary ware. <BR>We selected seven glasses constituted of SiO2-Al2O3-CaO-MgO-K2O-Na2O system for the coating glasses on the conventional glaze layer, and fabricated a double layer structure on a sanitary ware by firing. We also investigated the physical properties (glass transition temperature Tg, crystallization temperature Tc, liquidus temperature T1, and viscosity of the glass melts (η)) of the coating glass were measured. <BR>The microscopic observations of the cross-section at the interface between the graze layer and the coating glass layer showed three different mixing patterns as follows.<BR>(1) The graze layer and the coating glass layer were completely separated.<BR>(2) The graze layer and the coating glass layer were partially mixed.<BR>(3) The graze layer was partially exposed to the surface of the coating glass layer.<BR>From the results of the physical properties measurements of the coating glasses, it was found that the formation of double layer structure was controlled by the viscosity of glass melts and the thickness of the coating glass layer. Finally, we concluded that the accomplished double layer on the sanitary ware surface was suitable for improvement of durability and anti-contamination.
収録刊行物
-
- 資源と素材
-
資源と素材 126 (12), 691-696, 2010
一般社団法人 資源・素材学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205276108544
-
- NII論文ID
- 10027449280
-
- NII書誌ID
- AA12188381
-
- COI
- 1:CAS:528:DC%2BC3MXitFeltr4%3D
-
- ISSN
- 18840450
- 18816118
-
- NDL書誌ID
- 10923983
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可