炭酸水素カルシウム溶液から沈殿した炭酸カルシウムの形態制御

DOI Web Site Web Site 被引用文献25件 オープンアクセス

書誌事項

タイトル別名
  • Control of Crystal Shape and Modification of Calcium Carbonate Prepared by Precipitation from Calcium Hydrogencarbonate Solution
  • タンサン スイソ カルシウム ヨウエキ カラ チンデンシタ タンサン カルシウ

この論文をさがす

説明

The control of three modifications and crystal shape of calcium carbonate which precipitated by outgassing dissolved CO2 in calcium hydrogencarbonate solution was studied. The starting saturated solution (10.3×10-3mol CaCO3⋅dm-3) of calcium hydrogencarbonate was prepared by passing a stream of CO2 through the suspension of fine limestone powder at 2°C and then diluted with pure water to concentrations of 2.8-8.5×10-3mol CaCO3⋅dm-3 (initial supersaturation degree: 20-60). Characteristics of the precipitated calcium carbonate were determined by means of X-ray diffraction, infrared spectroscopy, scanning electron microscopy and chemical analysis. The formation region of three modifications was affected remarkably by synthetic conditions such as stirring, pH (6.2-8.0), heating temperature (20°-100°C) and concentration (initial supersaturation degree: 20-60) of calcium hydrogencarbonate solution. When calcium carbonate was precipitated by outgassing dissolved CO2 in calcium hydrogencarbonate solution under stirring with 240rpm, rhombohedral-like calcite about 10μm in size and prismoidal-like aragonite with 2×50μm in size and 99.7% in purity were independently formed at temperatures below 30°C and above 50°C respectively, while no vaterite was observed. However, vaterite was found as an independent phase by adding an alkaline solution of NaOH or NH4OH into calcium hydrogencarbonate solution without stirring. Especially, NH4OH solution was excellent as additive to form hexagonal plate-like crystals of vaterite as compared with NaOH solution. For example, hexagonal plate-like vaterite crystals 20μm in size and 99.7% in purity formed from calcium hydrogencarbonate solution with a supersaturation degree of 20 at pH 7.5-7.8 without stirring. These vaterite-crystals were unstable and transformed to the stable phase of hexagonal plate-like calcite by heating at 600°C. The uniform hexagonal plate-like crystals of calcium carbonate can be expected as a new functional inorganic filler for paper, plastics and rubber.

収録刊行物

被引用文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ