Alkali Passivation Mechanism of Sol-Gel Derived TiO<sub>2</sub>-SiO<sub>2</sub> Films Coated on Soda-Lime-Silica Glass Substrates

DOI Web Site Web Site 2 Citations

Bibliographic Information

Other Title
  • ソーダ石灰ガラス基板上に形成したゾル-ゲルTiO<sub>2</sub>-SiO<sub>2</sub>薄膜のアルカリパッシベイションメカニズム
  • ソーダ セッカイ ガラス キバンジョウ ニ ケイセイシタ ゾル ゲル TiO2

Search this article

Description

Alkali passivation mechanism of sol-gel derived TiO2-SiO2 glass films with different TiO2 contents coated on a soda-lime-silica glass substrate has been studied by SIMS and XPS analyses, and compared with the results of a sol-gel derived pure SiO2 film. An increase in TiO2 content in the TiO2-SiO2 film increased the sodium concentration in the film, which was induced by sodium migration from the glass substrate during the heat-treatment. It was also found that the chemical state of sodium ions in the TiO2-SiO2 films was different from the state of those either in the glass substrate or in the sol-gel derived pure SiO2 film. It is thus concluded that the TiO2-SiO2 films serve not as a barrier but as an effective getter of alkli ions and thereby effectively improve the weathering resistance of the glass substrate.

Journal

Citations (2)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top