Influence of Phase Transformation on Densification Behavior and Grain Growth of Fine Silicon Nitride Powder
-
- HIROTSURU Hideki
- Research Center, Denki Kagaku Kogyo K.K.
-
- MITOMO Mamoru
- National Institute for Research in Inorganic Materials
-
- NISHIMURA Toshiyuki
- National Institute for Research in Inorganic Materials
Bibliographic Information
- Other Title
-
- 窒化ケイ素微粉末の緻密化挙動及び粒成長に及ぼす相転移の影響
- チッカ ケイソ ビフンマツ ノ チミツカ キョドウ オヨビ リュウ セイチョウ
Search this article
Abstract
Fine and uniform silicon nitride powders having different α-content were prepared from commercial submicron powders by centrifugal sedimentation. The densified pre-sintered materials were fabricated from these powders by hot-pressing. The fine powders with similar particle size distribution showed the same densification behavior during hot-pressing. The microstructures of pre-sintered materials of the fine powders showed the fine and homogeneous microstructures, and the similar one irrespective of α content. The pre-sintered materials were annealed at 1800°C for 1h under 1MPa nitrogen atmosphere. The annealed material from the fine β powder showed the fine and homogeneous microstructure. On the other hand, the material from the fine α powder developed “in-situ composite” microstructure consisting of large grains and fine matrix grains by annealing. Because, the abnormal grain growth was caused by the α- to β-phase transformation during annealing. While, these results of the fine powders were compared with those of the commercial submicron powders.
Journal
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 104 (1205), 23-27, 1996
The Ceramic Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001205277102464
-
- NII Article ID
- 110002291304
-
- NII Book ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
- http://id.crossref.org/issn/09145400
-
- NDL BIB ID
- 3917988
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed