単体金属混合粉を用い作製したp型 (Bi<sub>2</sub>Te<sub>3</sub>)<sub>0.25</sub>(Sb<sub>2</sub>Te<sub>3</sub>)<sub>0.75</sub>熱電材料の微細構造及び熱電特性
書誌事項
- タイトル別名
-
- Relationship between Thermoelectric Properties and Microstructure on p-Type (Bi<sub>2</sub>Te<sub>3</sub>)<sub>0.25</sub>(Sb<sub>2</sub>Te<sub>3</sub>)<sub>0.75</sub> System Using Milled Powder
- タンタイ キンゾク コンゴウ フン オ モチイ サクセイシタ pガタ Bi2T
この論文をさがす
説明
We have developed p-type bismuth telluride of (Bi2Te3)0.25(Sb2Te3)0.75 system with modified PIES method, which shows the figure of merit and compressive strength of 1.6×10-3/K(25°C), and 9.8 MPa, respectively. Thermoelectric properties showed no anisotropy of electrical transport phenomena because the microstructure had no orientation of the grain growth. The improved compressive strength was presumably due to small grain sizes. The milling mechanism obeyed Kick's law.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 103 (1203), 1182-1187, 1995
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205277148288
-
- NII論文ID
- 110002291254
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
- http://id.crossref.org/issn/09145400
-
- NDL書誌ID
- 3638823
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可