Lager scale syntheses of surfactant-templated nanoporous silica spherical particles by the Stober method
-
- KAMBARA Kumiko
- Graduate School of Science and Engineering, Waseda University
-
- SHIMURA Naoki
- Graduate School of Science and Engineering, Waseda University
-
- OGAWA Makoto
- Department of Earth Sciences, Waseda University
書誌事項
- タイトル別名
-
- Larger Scale Syntheses of Surfactant-Templated Nanoporous Silica Spherical Particles by the Stoeber Method
- Larger scale syntheses of surfactant-templated nanoporous silica spherical particles by the Stöber method
この論文をさがす
抄録
The larger scale production of nanoporous silica spherical particles was investigated. The particles formed from aqueous solution containing cetyltrimethylammonium chloride, tetraethoxysilane (TEOS), methanol, and ammonia at room temperature and subsequent calcination in air at 550°C led the transformation of the particles to be nanoporous with retaining the original particle morphology. The increase in the TEOS amount in the starting solution was effective for larger scale synthesis without significant loss of particle size distribution. Average particle size varied from 50 nm to 320 nm and the BET surface area varied from 240 to 850 m2 g-1. Maximum product weight achieved was ca. 1 g from 100 g of starting solution; the value is one order greater than those obtained by previously reported starting solutions, where TEOS amount is much smaller. The particle size (to 1721 nm) and surface area (up to 1020 m2 g-1) were changed by the surfactant amount in the starting solutions.<br>
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 115 (1341), 315-318, 2007
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205277262720
-
- NII論文ID
- 110006249007
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 8816878
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可