Li<sub>2</sub>Ti<sub>3</sub>O<sub>7</sub>の相変化に対するNb<sub>2</sub>O<sub>5</sub>添加効果
書誌事項
- タイトル別名
-
- Effect of Nb<sub>2</sub>O<sub>5</sub> Addition on the Phase Change in Li<sub>2</sub>Ti<sub>3</sub>O<sub>7</sub>
- Li2Ti3O7 ノ ソウ ヘンカ ニ タイスル Nb2O5 テンカ コウカ
この論文をさがす
抄録
Nb2O5-added R (ramsdellite) phase was syntbesized by the melt-quenching method. Addition of 3 to 5mol% Nb2O5 accelerated the R→H (hexagonal phase) transformation, retarded the H→S+r (spinel and rutile) successive decomosition reaction, and stabilized the H phase at high temperatures. These effects were possibly caused by the preferential incorporation of Nb2O5 in the H phase. The phase changes in the Nb2O5-added R phase occurred similarly to the non-added R phase following the route quenched-R→H→S+r→R during heating and R→H→S+r during cooling, respectively. The R phase containing 3mol% Nb2O5 was heated to 850°C at 2°C/min in air, then quenched, and the H phase was obtained although very small amounts of rutile and spinal were contained. Lattice constants of the obtained H phase were a=0.8777(8)nm and c=6.988(2)nm, and the effect of Nb2O5 addition was hardly recognized. The linear thermal expansion coefficient of the H phase was determined to be α=1.34×10-5K-1 between room temperature and 900°C. Investigation on the phase changes in the H phase during heating clarified those in the R phase.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 101 (1174), 654-658, 1993
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205277392128
-
- NII論文ID
- 110002290378
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 3825432
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可