大型陶磁器の鋳込み成形における内面盛上りの発生の防止

DOI Web Site Web Site 参考文献9件 オープンアクセス
  • 森 謙一郎
    豊橋技術科学大学生産システム工学系
  • 片田 由人
    豊橋技術科学大学大学院修士課程工学研究科生産システム工学専攻
  • 梅田 学
    (株) INAX 技術研究所

書誌事項

タイトル別名
  • Prevention of Occurrence of Internal Bulge in Slip Casting of Large Potteries

この論文をさがす

説明

The mechanism of the formation of an internal bulge appearing as a local increase in wall thickness in the slip casting of large potteries was investigated to prevent occurrence of cracks in dried green bodies. Because it is not easy to observe moisture suction and deposition inside a plaster mold, a simple plate mold was used in the experiment. Moisture suction in the joining region during the casting was enhanced by breaking the alignment of particles due to the collision between the fronts of the slurry; thus, the wall thickness in the joining region increased owing to the acceleration of the growth of deposit. An internal bulge was formed by the difference in the growth of deposits between the joining and peripheral regions. It was found in the slip casting of a model washbasin that the occurrence of internal bulge is prevented by vibrating the plaster mold during the pouring of the slurry.<br>

収録刊行物

参考文献 (9)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ