La<sub>1-<i>X</i></sub>Sr<sub><i>X</i></sub>MnO<sub>3</sub>の焼結と電気伝導度

DOI Web Site Web Site 被引用文献7件

書誌事項

タイトル別名
  • Sintering and Electrical Conductivity of La<sub>1-<i>X</i></sub>Sr<sub><i>X</i></sub>MnO<sub>3</sub>
  • La1-xSrxMnO3 ノ ショウケツ ト デンキ デンドウド エイブン

この論文をさがす

抄録

The sinterability and electrical conductivity of La1-XSrXMnO3 were studied as a function of calcination temperature (500° to 1200°C), firing temperature (1200° to 1500°C), atmosphere (air or vacuum) Sr content (0≤X≤0.5), and cation deficiency. Both density and electrical conductivity increased with either decreasing calcination temperature or increasing firing temperature. Sintering in vacuum increased the density and decreased the electrical conductivity. The content of Sr, X, influenced these characteristics remarkably, The density decreased drastically with increasing X, giving the lowest value at X=0.4. On the other hand, the electrical conductivity increased with increasing X, giving the maximum value at X=0.15. The temperature dependence of the electrical conductivity of La0.85Sr0.15MnO3 was confirmed to be consistent with the small polaron hopping transport mechanism. The cation deficiency improved the sinterability of La1-XSrXMnO3 ceramics. These results indicated that the density and electrical conductivity of La1-XSrXMnO3 are largely influenced by the concentration of incorporated oxygen.

収録刊行物

被引用文献 (7)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ