SiCウイスカー強化MoSi<sub>2</sub>複合材料の機械的性質

DOI Web Site Web Site 被引用文献3件 参考文献20件

書誌事項

タイトル別名
  • Mechanical Properties of SiC-Whisker-Reinforced MoSi<sub>2</sub> Composites
  • SiC ウイスカー キョウカ MoSi2 フクゴウ ザイリョウ ノ キカイテキ

この論文をさがす

説明

Molybdenum disilicide (MoSi2) is considered as a candidate material for high temperature structural applications, particularly in oxidizing environments. In the present study, SiC-whisker reinforcement has been applied to improve the mechanical properties such as fracture strength and fracture resistance at room temperature as well as creep resistance at elevated temperature. Almost dense SiC-whisker-reinforced MoSi2 composites containing up to 20vol% whisker were fabricated by hot-pressing at 1750°C. Due to the well-dispersed composite structure with fine grained matrix, the composites showed much higher bending strength than unreinforced materials; the average 4-point bending strength increased from 350MPa for MoSi2 to 870MPa for MoSi2-20%SiCw. The fracture resistance also considerably improved by the SiC-whisker reinforcement. The composites exhibited increasing R-curve behavior and the plateau values were about 23-34% higher compared to that of the unreinforced materials. Crack bridging was found to be mainly responsible for the toughening contribution. Creep resistance was remarkably increased by the suppression effect of SiC-whisker on the grain boundary sliding, which was confirmed to be an important deformation mechanism in MoSi2 polycrystals.

収録刊行物

被引用文献 (3)*注記

もっと見る

参考文献 (20)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ