PbO-GeO<sub>2</sub>ガラス中のGeの配位状態のEXAFS研究

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • EXAFS Study on the Coordination State of Germanium in PbO-GeO<sub>2</sub> Glasses
  • PbO GeO2 ガラスチュウ ノ Ge ノ ハイイ ジョウタイ ノ EXAF
  • Relation between Structure and Optical Nonlinearity
  • 構造と光学非線形性の関係

この論文をさがす

抄録

The coordination state of Ge ions in PbO-GeO2 glasses was examined using EXAFS. It was found that a part of Ge ions changed from 4-fold to 6-fold coordination state on addition of PbO, which had been expected from the property-composition relations. The fraction of 6-fold coordinated Ge ions, N6, increased with increasing PbO content up to 20mol%, then decreased on further increase in PbO content. However, the maximum N6 was about 13% and twice as small as that in binary alkali germanate glasses. The refractive index of the glasses, n, increased with increasing PbO content, showing a very faint hump around 20mol% PbO, and third-order nonlinear optical susceptibility, χ(3), monotonously increased from 1.0×10-13 esu at PbO=0 to 5.6×10-13 esu at PbO=40mol% with an increase in PbO content. The absence of germanate anomaly in nor χ(3)-composition relation was explained by the smaller effect of change in coordination state of Ge ions in comparison with that by PbO addition.

収録刊行物

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ