- Preparation of Mn-Modified Tetragonal PZT Ceramics and Their Pyroelectric Properties
- Preparation of Mn Modified Tetragonal PZ
この論文をさがす
抄録
The results of this study are summarized as follows:<br>(1) High density tetragonal PZT ceramics with compositions of {Pb(ZrxTi1-x)O3+0.5mass% MnO2}, where x=0.10-0.50, were successfully synthesized by hot isostatic pressing.<br>(2) HIPed samples with x=0.20 had the highest bulk density of 7.82g/cm3, which is 98.2% of the theoretical density.<br>(3) The Curie temperature TC for PZT ceramics with x=0.10-0.50 decreased linearly with an increase in Zr content. The rate of linear decrease m calculated from the linear plot of TC with x was approximately 3.0°C/mol% Zr.<br>(4) The PZT sample with x=0.20 exhibited the highest figure of merit F.M. of around 2.1×10-11C·cm/J. Assuming that the volume specific heat Cv of the present sample with x=0.20 and that of PZTZBM ceramic with x=0.30 are the same (3.1J/cm3·K), the F.M. for voltage responsivity of pyroelectric IR sensors fabricated using these ceramics which have the same tetragonal structure should be nearly equal.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 104 (1208), 259-263, 1996
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205278606848
-
- NII論文ID
- 110002291351
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 3947882
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可