Preparation of Dense Piezoelectric PbNb2O6 Ceramics from Powders with Low-Temperature Form

  • LEE Ho Sung
    Graduate School of Science and Technology, Keio University
  • KIMURA Toshio
    Graduate School of Science and Technology, Keio University

Bibliographic Information

Other Title
  • 低温相粉体を用いた緻密な圧電性 PbNb<sub>2</sub>O<sub>6</sub> の作製

Search this article

Abstract

The effect of microstructure on dielectric and piezoelectric properties of PbNb2O6 was studied to examine the possibility of using powder with the low-temperature rhombohedral form for the preparation of piezoelectric PbNb2O6 ceramics. Dense, fine-grained PbNb2O6 ceramics with good piezoelectric property with the maximum kt value of 0.315 were obtained by rapid heating and isothermal soaking at 1250°C of powders with particle size between 0.7 and 1.0 μm. The use of coarse powder resulted in the development of large grains and pores caused by exaggerated grain growth induced by phase transformation from the low- to high-temperature forms. Isothermal soaking at 1300°C resulted in the formation of a duplex structure. These structural defects reduced the piezoelectric property.<br>

Journal

Citations (2)*help

See more

References(40)*help

See more

Details 詳細情報について

Report a problem

Back to top