一軸引張応力下における稲田花崗岩の疲労特性と寿命予測

DOI Web Site 参考文献25件

書誌事項

タイトル別名
  • Fatigue Properties and Life Expectancy of Inada Granite under Uniaxial Tension
  • イチジク ヒッパリ オウリョク カ ニ オケル イナダ ハナオカガン ノ ヒロウ トクセイ ト ジュミョウ ヨソク

この論文をさがす

抄録

Uniaxial tension cyclic loading and creep tests were carried out on Inada granite aiming to clarify effects of stress amplitude and loading rate on fatigue behavior. Relationship between fatigue life, deformation behavior and AE activity were also examined. It was found that time to failure in cyclic loading test became shorter than that in creep test for low applied stress. This indicates stress amplitude has a significant effect on fatigue failure. The amount of fatigue damage per cycle increased with decrease in loading rate when the same maximum stress was applied. This is thought to be cause of decrease in fatigue life with decrease in loading rate. On the other hand, the amount of fatigue damage per cycle and fatigue life did not depend on loading rate when the same maximum stress ratio, which was normalized by the uniaxial tensile strength at each loading rate, was applied. Fatigue life of a specimen showing less strain increment tended to be longer and the relationship between the minimum value in the strain increment and fatigue life was represented by a line regardless of loading rate and maximum stress. AE event rate as well as strain increment was inversely proportion to life expectancy before failure. Ratio of AE event rate in unloading to loading began to increase just before failure. These results show that strain increment and AE event are useful parameter to predict fatigue failure.

収録刊行物

  • 資源と素材

    資源と素材 129 (7), 418-424, 2013

    一般社団法人 資源・素材学会

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ