Synthesis and characterization of NiFe2O4 nanopowders via spray pyrolysis
-
- JUNG Dae Soo
- Department of Chemical Engineering, Konkuk University
-
- JANG Hee Chan
- Department of Chemical Engineering, Konkuk University
-
- LEE Man-Jong
- Department of Advanced Technology Fusion, Konkuk University
-
- JUNG Kyeong Youl
- Department of Chemical Engineering, Kongju National University
-
- KANG Yun Chan
- Department of Chemical Engineering, Konkuk University
この論文をさがす
抄録
NiFe2O4 powders with large-sized, hollow, and thin wall structures were directly prepared by spray pyrolysis from a spray solution containing citric acid. These as-prepared powders converted into nanosized NiFe2O4 powders after post-treatment at high temperatures between 600 and 1000°C. Phase-pure NiFe2O4 powders were obtained at post-treatment temperatures between 700 and 1000°C. When the post-treatment temperatures were increased from 700 to 1000°C, the BET surface areas of the NiFe2O4 powders decreased from 23.4 to 11.8 m2/g and their mean sizes increased from 47.8 to 94.7 nm, respectively. The saturation magnetizations of the powders changed from 32 to 44 emu/g according to changes in the post-treatment temperatures. The coercivities of the powders post-treated at temperatures of 700 and 800°C were 118 and 130 Oe, respectively.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 117 (1370), 1069-1073, 2009
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205282534016
-
- NII論文ID
- 130000304922
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 10374125
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可