Electrochemical reforming of CH4-CO2 gas using porous Gd-doped ceria electrolyte with Ni and Ru electrodes
-
- MATAYOSHI Shotaro
- Department of Chemistry, Biotechnology, and Chemical Engineering, Kagoshima University
-
- HIRATA Yoshihiro
- Department of Chemistry, Biotechnology, and Chemical Engineering, Kagoshima University
-
- SAMESHIMA Soichiro
- Department of Chemistry, Biotechnology, and Chemical Engineering, Kagoshima University
-
- MATSUNAGA Naoki
- Department of Chemistry, Biotechnology, and Chemical Engineering, Kagoshima University
-
- TERASAWA Yujin
- Department of Chemistry, Biotechnology, and Chemical Engineering, Kagoshima University
この論文をさがす
抄録
Electrochemical reforming of 50% CH4-50% CO2 mixed gas was investigated using the cell of Ni or Ru-GDC (Gd-doped ceria) cathode/porous GDC electrolyte/Ni, Ru or SrRuO3-GDC anode system at 400°-800°C under 1.25 V/cm of electric field strength. Use of Ni as anode accelerated the decomposition of CH4 (CH4 → C + 2H2) and caused the blockage of supplied gas because of the deposition of carbon in the open spaces of anode. On the other hand, Ni in cathode worked well to reduce CO2 to CO and O2- ions (CO2 + 2e- → CO + O2-). Use of Ru in both electrodes gave little problems to oxidize CH4 in anode (CH4 + O2- → CO + 2H2 + 2e-) and to reduce CO2 in cathode. SrRuO3 in anode worked also to oxidize CH4. This oxide reacted with H2 produced in the reforming of CH4 to form Ru and Sr. Sr evaporated at 800°C during the reforming. Stable formation of a H2-CO fuel was measured for 11-13 h at 800°C using the cells with Ni or Ru cathode and Ru anode.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 117 (1371), 1147-1152, 2009
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205283530624
-
- NII論文ID
- 130000304938
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 10410686
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可