The 62th CerSJ Awards for Academic Achievement in Ceramic Science and Technology: Wet preparation and characterization of ScSZ thin film electrolyte on micro-cathode supports
-
- YAMAGUCHI Toshiaki
- National Institute of Advanced Industrial Science and Technology
書誌事項
- タイトル別名
-
- Wet preparation and characterization of ScSZ thin film electrolyte on micro-cathode supports
この論文をさがす
抄録
Preparation of a dense Sc2O3-doped ZrO2 (ScSZ) thin film electrolyte on a microtubular cathode support was accomplished using wet coating process and subsequent co-sintering. The microtubular (La,Sr)MnO3 (LSM) cathode support had a 1.6 mm diameter and approximately 30% open porosity. The cell, with 20 μm thick ScSZ electrolyte, was electrochemically evaluated in a humidified (3% H2O) hydrogen atmosphere. The microtubular cells exhibited a stable open circuit voltage above 1.05 V in the temperature range from 550 to 750°C. Maximum power densities of 46.5, 163.2 and 452.8 mW/cm2 were generated at 550, 650 and 750°C, respectively. The results indicate that this preparation of a thin film ScSZ electrolyte effectively realized a stable, high performance LSM-supported micro SOFC.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 117 (1362), 139-142, 2009
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205284413312
-
- NII論文ID
- 110007044066
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 9781692
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可