Fabrication of c-axis-oriented potassium strontium niobate (KSr2Nb5O15) ceramics by a rotating magnetic field and electrical property
-
- TANAKA Satoshi
- Department of Materials Science and Technology, Nagaoka University of Technology
-
- TAKAHASHI Takuma
- Department of Materials Science and Technology, Nagaoka University of Technology
-
- FURUSHIMA Ryoichi
- Department of Materials Science and Technology, Nagaoka University of Technology
-
- MAKIYA Atsushi
- Department of Materials Science and Technology, Nagaoka University of Technology
-
- UEMATSU Keizo
- Department of Materials Science and Technology, Nagaoka University of Technology
この論文をさがす
抄録
Fabrication and property of c-axis-oriented KSr2Nb5O15 (KSN) ceramics were examined. Particle-oriented KSN was fabricated by using a rotating magnetic field and subsequent sintering. KSN fine powder was prepared by conventional solid-state reaction and grinding processing. C-axis-oriented KSN green compact was fabricated in a rotating magnetic field 10 Tesla. The resulting green body was sintered at 1473 K for 6 h and then at 1525 K for 2 h to prevent exaggerated grain growth. C-axis-oriented KSN ceramics with relative density 92% was obtained. In XRD, peaks from the c-planes, such as 001 and 002, were very strong at the horizontal cross section of the sintered specimens. The ferroelectric and piezoelectric property along to c-axis was also improved to 21 µC/cm2 and d33 = 101 pC/N by orientation structure.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 118 (1380), 722-725, 2010
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205285550208
-
- NII論文ID
- 130000304624
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 10770791
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可