- KITA Ken’ichiro
- National Institute of Advanced Industrial Science and Technology (AIST)
-
- KONDO Naoki
- National Institute of Advanced Industrial Science and Technology (AIST)
-
- IZUTSU Yasuhisa
- Stereo Fabric Research Association
-
- KITA Hideki
- National Institute of Advanced Industrial Science and Technology (AIST)
この論文をさがす
抄録
This paper describes a novel experiment involving the joining of alumina using a polymer blend method and Al foil. Alumina pieces were dipped into a polymer blend containing polycarbosilane and polymethylphenylsiloxane, which is a kind of polysiloxane. After curing and ceramization of the polymer on the alumina pieces, the pieces sandwiching Al foil were heated under vacuum at 1073 K. The samples near the center of the joining area (SC samples) were mainly composed of metal Si without any cracks, and their average tensile strength was very high, approximately 252 MPa. On the other hand, the samples on the periphery of the joining area (SP samples) were mainly composed of a carbon-rich substance such as aluminum carbide with deep cavities, and their average tensile strength was poor in comparison to the SC samples, approximately 56.9 MPa.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 120 (1406), 408-412, 2012
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205285620224
-
- NII論文ID
- 130004480100
- 40019427961
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 023971702
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可