Synthesis and phase transition behavior of w-doped VO2(A) nanorods
-
- JI Shidong
- Department of Scientific and Engineering Simulation, Nagoya Institute of Technology
-
- ZHAO Yangang
- Department of Scientific and Engineering Simulation, Nagoya Institute of Technology
-
- ZHANG Feng
- Department of Scientific and Engineering Simulation, Nagoya Institute of Technology
-
- JIN Ping
- National Institute of Advanced Industrial Science & Technology (AIST) Shanghai Institute of Ceramics, CAS
この論文をさがす
抄録
In this paper, pure and w-doped VO2(A) nanorods were synthesized via the reduction of V2O5 with oxalic acid through hydrothermal treatment and characterized by XRD, SEM and DSC. The study about the influence of w-doping on its phase transition and stability properties was carried out for the first time on the best of our knowledge. The doping of tungsten decreased the phase transition temperature of VO2(A) just as it does in the case of rutile VO2(R). The doping limitation of tungsten for pure VO2(A) was estimated to be about 0.5–0.75 at. %, whereas over doping of tungsten led to the destabilization of VO2(A) phase. Based on the experimental results, the solution reaction process should be such that VO2(B) was first formed at lower temperature or shorter time, and then transformed to VO2(A) or VO2(R) during hydrothermal treatment. Furthermore, inhomogeneous doping of tungsten in VO2 during the crystallization from the solution was revealed by DSC measurements.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 118 (1382), 867-871, 2010
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205285710464
-
- NII論文ID
- 130000420705
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 10831912
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可