Influence of B<sub>2</sub>O<sub>3</sub> on sintering behavior and the dielectric properties of Li<sub>2</sub>MgSiO<sub>4</sub> ceramics

DOI Web Site Web Site 12 References

Bibliographic Information

Other Title
  • Influence of B₂O₃ on sintering behavior and the dielectric properties of Li₂MgSiO₄ ceramics

Search this article

Description

The influence of B2O3 additives on the sintering behavior, microstructure, and dielectric properties of Li2MgSiO4 (LMS) ceramics was investigated. The experimental results showed that doping of LMS ceramics with 2 wt % B2O3 caused a decrease in the sintering temperature from 1250 to 810°C. The ceramics produced were dense with a well-crystallized microstructure where predominantly fine grains of Li2MgSiO4 were formed. The dielectric properties appeared to be dependent on microstructure. The measured dielectric values of 2% B2O3-doped LMS ceramics (εr = 6.61 and tan δ = 1.6 × 10−4 at 1 MHz and εr = 5.84 and tan δ = 7.43 × 10−5 at 8 GHz) indicate their potential for use in applications which require the involvement of low temperature co-fired ceramics (LTCC).

Journal

References(12)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top