- Fundamental Studies on Detergency. II.
- センジョウ サヨウ ノ キソ ケンキュウ 2 チカンド オ イ ニ スル ポリ
- Solid Surface Tension of Polyvinylformal and Cellulose Acetate Having Different Degree of Substitution
- 置換度を異にするポリビニルホルマール及びセルロースアセタートの固体表面張力
この論文をさがす
抄録
Surface tensions (γs) and their surface tension components (γsd, γsP) of polyvinylformal (VinylonR, formalization degree 9.463.1 mol%), cellulose acetate (acetylation degree 38.443.8%), cellophane, and iron (III) oxinate were calculated from extended Fowkes' equation and Wu's equation. (Table-2, 3, 4) <BR>The polar force component values (γsP) from Wu's equation were a little bigger than those from extended Fowkes' equation. <BR>The polar force components (γsP) of Vinylon showed the minimum value when the formalization degree was about 35%. This indicated that the surface tension of Vinylon was minimum at the same formalization degree. <BR>It was also revealed that the polar force components (γsP) of cellulose acetate and cellophane decreased with increasing the acetylation degree whereas the surface tension (γs) decreased with increasing the acetylation degree. <BR>The surface tension values listed in Table-2, 3, 4 may be helpful for calculating the work of adhesion (Wa) in detergency and adhesion studies.
収録刊行物
-
- 油化学
-
油化学 28 (12), 902-905, 1979
公益社団法人 日本油化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205332222592
-
- NII論文ID
- 130001015921
-
- NII書誌ID
- AN00245435
-
- ISSN
- 0513398X
- 18842003
-
- NDL書誌ID
- 2071855
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可