- KUWATA Tsutomu
- Department of Applied Chemistry, Faculty of Engineering, Tokyo University
-
- KUMANOTANI Jyu
- Department of Applied Chemistry, Faculty of Engineering, Tokyo University
-
- YANASE Kunio
- Nippon Gosei K.K.
-
- KITAMURA Takuo
- Fuji Seitetsu K.K.
Bibliographic Information
- Other Title
-
- フェノール系樹脂に関する研究 (第3報)
- フェノールケイ ジュシ ニ カンスル ケンキュウ 3
- Preparation of Rosin Modified Phenolics using Phenol Resol
- レゾールを用いるロジン変性フェノール樹脂の合成
Search this article
Abstract
For improvement of oil-solubility, authors have studied about the preparative methods of resol and rosin-modified phenolics using the resol as follows : <BR>1) Phenol resol was obtained by the reaction of acid condensation at pH 15 and at 50°C for eight to ten hours from the methylolated phenol which was prepared by the reaction of phenol (1mol) with formaldehyde (0.83.0mol) in the presence of sodium hydroxide (0.2mol, 45% concentration) at room temperature for a day. Average composition of the resol is shown by the _??_OH CH2 OH CH2OH formula in case of the mole-ratio of phenol to formaldehyde being 1 : 1.<BR>2) Some kinds of rosin-modified phenolics were prepared by heating rosin, resol and glycerine, and the relations of oil-solubility and softening point of the resins to the properties and contents of the resol were examined. Oil-solubility of the rosin-modified phenolics prepared is solely affected by the resol content and is independent for the kinds of the resol prepared under various conditions.<BR>The limit of resol content allowing oil-solubility is 25% by weight. When the resol to be used is left for more than ten days, the lowering of softening point of the resins can be seen, compared with the case using the resol soon after the preparation.<BR>The rosin-modified phenolics prepared here have shown excellent oil-solubility inspite of their high softening points (140180°C).
Journal
-
- Journal of Japan Oil Chemists' Society
-
Journal of Japan Oil Chemists' Society 10 (11), 710-716, 1961
Japan Oil Chemists' Society
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205333179136
-
- NII Article ID
- 130001009212
-
- NII Book ID
- AN00245435
-
- ISSN
- 0513398X
- 18842003
-
- NDL BIB ID
- 9213875
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed